In this work,
tribological performance of pure poly-tetra-fluoro-ethylene (PTFE), 25%bronze
filled PTFE composite and 40%bronze filled PTFE composite sliding against
stainless steel under dry sliding environment were studied. A pin-on-disc tribometer
is used for evaluating the friction and wear behavior of PTFE polymer and its
composites. The tribological tests were conducted at applied loads of 50N,
100N, and 150N and at sliding speeds of 1.0, 1.5 and 2.0 m/s. The results show
that the PTFE+40wt.% bronze composite is the best tribological behavior. As a
result of study, the coefficient of friction and specific wear rate of PTFE
composite were reduced by the addition of bronze filler. Finally, an optical
microscope was used to examine the wear mechanism of pure PTFE and PTFE
composites with bronze filler.
Bu deneysel çalışmada, katkısız
poli-tetra-flor-etilen (PTFE) polimeri ile %25 bronz katkılı PTFE kompoziti ve
%40 bronz katkılı PTFE kompozitlerin, kuru kayma şartları altında paslanmaz
çelik malzemeye karşı tribolojik performansları incelenmiştir. Tribolojik
testler, pim-disk aşınma cihazında ve oda sıcaklığında gerçekleştirilmiştir.
Aşınma ve sürtünme testleri, 50N, 100N ve 150N yüklerde ve 1.0, 1.5 ve 2.0m/s
kayma hızlarında yapılmıştır. Aşınma test sonuçlarına göre, %40 bronz katkılı
PTFE kompozitinin sürtünme katsayısı değerleri ile spesifik aşınma oranı değerlerinin
katkısız PTFE ve %25 bronz katkılı PTFE’ye göre daha düşük olduğu tespit
edilmiştir. PTFE ve bronz katkılı PTFE kompozitlerinin aşınma yüzeylerini
incelemek için optik mikroskop kullanılmıştır. Bronz katkılı PTFE kompozitlerin
aşınma mekanizması adhezif ve abrazif aşınma şeklinde gerçekleşmiştir.
Primary Language | Turkish |
---|---|
Subjects | Engineering |
Journal Section | Articles |
Authors | |
Publication Date | June 15, 2015 |
Published in Issue | Year 2015 Issue: 034 |
HAZİRAN 2020'den itibaren Journal of Scientific Reports-A adı altında ingilizce olarak yayın hayatına devam edecektir.