Microstructure and Wear Properties of Hardfacings Obtained Using Submerged Arc Welding Powders Containing Ferroniobium and Ferroboron
Ferroniyobyum ve Ferrobor İçeren Tozaltı Kaynak Tozları ile Elde Edilen Kaplamaların Mikroyapı ve Aşınma Özelliklerinin Araştırılması

Mustafa KAPTANOĞLU [1] , Mehmet EROĞLU [2]

258 619

In this study, submerged arc welding powders containing ferroniobium and ferroboron at four different rates combined with S1 welding wires subjected to the welding test with the aim of hardfacing on SAE 1020 steel surface. As a results of welding tests, microstructure, hardness and wear properties of hardfacings were investigated. With an increase in amounts of ferroniobium and ferroboron in welding powders, both percentage of boride structure located in hardfacing microstructure were increased, and the hardness increased. Therefore, the wear losses decreased. The highest hardness result was determined with the hardfacing obtained from the welding powder containing %12 ferroniobium and %10 ferroboron as 48 HRC, the lowest hardness result was determined with the hardfacing obtained from the welding powder containing %3 ferroniobium and %2,5 ferroboron as 41 HRC

Bu çalışmada, SAE 1020 çelik yüzeylerde sert dolgu kaplama elde etmek amacıyla, 4 farklı oranda ferroniyobyum ve ferrobor içeren tozaltı kaynak tozları, S1 kaynak telleri ile kombine edilerek tozaltı kaynak testlerine tabi tutulmuştur. Gerçekleştirilen kaynak testleri neticesinde; elde edilen kaplamaların mikroyapı, sertlik ve aşınma özellikleri incelenmiştir. Artan miktarlardaki ferroniyobyum ve ferroborun toz bünyesinde kullanılmasıyla elde edilen kaplama mikroyapılarında yer alan borürlerin yüzdesi artmış, sertlikler artmış ve kaplamaların aşınma kayıpları azalmıştır. En yüksek sertlikler %12 ferroniyobyum ve %10 ferrobor içeren kaynak tozu ile elde edilen kaplamada 48 HRC olarak tespit edilirken, en düşük sertlikler ise %3 ferroniyobyum ve %2.5 ferrobor içeren kaynak tozu ile elde edilen kaplamada 41 HRC olarak tespit edilmiştir.

  • [6] Kanjilal P., Pal T.K., Majumdar S.K. (2006) ‘’ Combined effect of flux and welding parameters on chemical composition and mechanical properties of submerged arc weld metal’’, Journal of Materials Processing Technology, 171, 223-231.
  • [7] Mercado A.M.P., Lopez V.M., Rosales J.D., Diaz P.E., Valdez E.D. (2009). Effect of TiO2-containing fluxes on the mechanical properties and microstructure in submerged-arc weld steels, 60, 1, 36-39.
  • [10] www.askaynak.com.tr, (25 Kasım 2016).
  • [11] www.gedikkaynak.com.tr, (25 Kasım 2016).
  • [12] www.oerlikon.com.tr, ( 25 Kasım 2016).
  • [13] Berns H., Fischer A. (1987) ‘’Microstructure of Fe-Cr -C-B alloys addition of Nb,Ti and B’’ Metallography, 20:401-429.
  • [14] Ke Y. , Zhi-xi Z., Wang- qin H., Ye-feng B., Yang-Feng J. (2011). ‘’A new type of submerged arc flux cored wired used for hardfacing continous casting rolls’’ Journal of iron and steel research international 18(11), 74-79.
  • [15] Singh B., Khan Z.A., Siddiquee A.N. October 2013 ’’Review on effect offlux composition on its behavior and bead geometry in submerged arc welding(SAW), Journal of Mechanical Engineering Research, Vol. 5(7), pp.12-12.
  • [16] Kim1 J.T., Hong S.H., Park H.J., Park G.H.,. Suh J.Y, Park J.M. Kim K.B. (2015). ‘Influence of microstructural evolution on mechanical behavior of Fe-Nb-B ultrafine composites with a correlation to elastic modulus and hardness’’, Journal of Alloys and Compounds 2015, (10.1016/j.jallcom.2015.05.246).
  • [17] Koga G.Y., Nogueira R.P., Roche V., Yavari A.R.,Melle A.K., Gallegod J., Bolfarini C., Kiminami C.S., Botta W.J., (2014), ‘’Corrosion properties of Fe–Cr–Nb–B amorphous alloys and coatings’’, Surface & Coatings Technology 254, 238–243.
  • [18] Kim2 J.T., Hong S.H., ParkH.J. , Kim Y.S. Park G.Y. Park J.Y. Lee N., Seo Y. ,Park J.M. ,Kim K.B., (2015), ‘’Improving the plasticity and strength of Fe–Nb–B ultrafine eutectic composite’’, Materials and Design 76 190–195.
  • [19] Savaşkan T. (2009), Malzeme Bilgisi Ve Muayenesi, Genişletilmiş 5.Baskı Trabzon.
  • [20] Azimi G.H., (2012).’’ Microstructure and wear properties of Fe-Cr-C and Fe-Cr-Nb-C clads on carbon steel by TIG surfacing process’’, Int. J.Surface Science andEngineering,Vol.6,Nos. ½.
  • [21] Wang Q. Xiaoyan L., (2010), ‘‘Effects of Nb, V, and W on Microstructureand Abrasion Resistance of Fe-Cr-C Hardfacing Alloys’ ,Supplement to the welding journal, Welding Journal Page 133-139.
  • [22] Kılınc B., Durmaz Abakay M., Sen U. , Sen S., (2015), ‘’Wear behavior of the surface alloyed AISI 1020 steel with Fe-Nb-B by TIG welding technique’’, AIP Conference Proceedings 1653, 020058 ; doi: 10.1063/1.4914249.
  • [16] Kim1 J.T., Hong S.H., Park H.J., Park G.H.,. Suh J.Y, Park J.M. Kim K.B. (2015). ‘Influence of microstructural evolution on mechanical behavior of Fe-Nb-B ultrafine composites with a correlation to elastic modulus and hardness’’, Journal of Alloys and Compounds 2015, (10.1016/j.jallcom.2015.05.246).
  • [17] Koga G.Y., Nogueira R.P., Roche V., Yavari A.R.,Melle A.K., Gallegod J., Bolfarini C., Kiminami C.S., Botta W.J., (2014), ‘’Corrosion properties of Fe–Cr–Nb–B amorphous alloys and coatings’’, Surface & Coatings Technology 254, 238–243.
  • [18] Kim2 J.T., Hong S.H., ParkH.J. , Kim Y.S. Park G.Y. Park J.Y. Lee N., Seo Y. ,Park J.M. ,Kim K.B., (2015), ‘’Improving the plasticity and strength of Fe–Nb–B ultrafine eutectic composite’’, Materials and Design 76 190–195.
  • [19] Savaşkan T. (2009), Malzeme Bilgisi Ve Muayenesi, Genişletilmiş 5.Baskı Trabzon.
  • [20] Azimi G.H., (2012).’’ Microstructure and wear properties of Fe-Cr-C and Fe-Cr-Nb-C clads on carbon steel by TIG surfacing process’’, Int. J.Surface Science andEngineering,Vol.6,Nos. ½.
  • [21] Wang Q. Xiaoyan L., (2010), ‘‘Effects of Nb, V, and W on Microstructureand Abrasion Resistance of Fe-Cr-C Hardfacing Alloys’ ,Supplement to the welding journal, Welding Journal Page 133-139.
  • [22] Kılınc B., Durmaz Abakay M., Sen U. , Sen S., (2015), ‘’Wear behavior of the surface alloyed AISI 1020 steel with Fe-Nb-B by TIG welding technique’’, AIP Conference Proceedings 1653, 020058 ; doi: 10.1063/1.4914249.
Konular Mühendislik
Dergi Bölümü Araştırma Makalesi
Yazarlar

Yazar: Mustafa KAPTANOĞLU
Kurum: FIRAT UNIV
Ülke: Turkey


Yazar: Mehmet EROĞLU
Kurum: FIRAT UNIV

Bibtex @araştırma makalesi { ksujes292373, journal = {Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi}, issn = {}, eissn = {1309-1751}, address = {Kahramanmaraş Sütçü İmam Üniversitesi}, year = {2017}, volume = {20}, pages = {64 - 75}, doi = {10.17780/ksujes.292373}, title = {Ferroniyobyum ve Ferrobor İçeren Tozaltı Kaynak Tozları ile Elde Edilen Kaplamaların Mikroyapı ve Aşınma Özelliklerinin Araştırılması}, key = {cite}, author = {KAPTANOĞLU, Mustafa and EROĞLU, Mehmet} }
APA KAPTANOĞLU, M , EROĞLU, M . (2017). Ferroniyobyum ve Ferrobor İçeren Tozaltı Kaynak Tozları ile Elde Edilen Kaplamaların Mikroyapı ve Aşınma Özelliklerinin Araştırılması. Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi, 20 (1), 64-75. DOI: 10.17780/ksujes.292373
MLA KAPTANOĞLU, M , EROĞLU, M . "Ferroniyobyum ve Ferrobor İçeren Tozaltı Kaynak Tozları ile Elde Edilen Kaplamaların Mikroyapı ve Aşınma Özelliklerinin Araştırılması". Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi 20 (2017): 64-75 <http://jes.ksu.edu.tr/issue/28695/292373>
Chicago KAPTANOĞLU, M , EROĞLU, M . "Ferroniyobyum ve Ferrobor İçeren Tozaltı Kaynak Tozları ile Elde Edilen Kaplamaların Mikroyapı ve Aşınma Özelliklerinin Araştırılması". Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi 20 (2017): 64-75
RIS TY - JOUR T1 - Ferroniyobyum ve Ferrobor İçeren Tozaltı Kaynak Tozları ile Elde Edilen Kaplamaların Mikroyapı ve Aşınma Özelliklerinin Araştırılması AU - Mustafa KAPTANOĞLU , Mehmet EROĞLU Y1 - 2017 PY - 2017 N1 - doi: 10.17780/ksujes.292373 DO - 10.17780/ksujes.292373 T2 - Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi JF - Journal JO - JOR SP - 64 EP - 75 VL - 20 IS - 1 SN - -1309-1751 M3 - doi: 10.17780/ksujes.292373 UR - http://dx.doi.org/10.17780/ksujes.292373 Y2 - 2018 ER -
EndNote %0 Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi Ferroniyobyum ve Ferrobor İçeren Tozaltı Kaynak Tozları ile Elde Edilen Kaplamaların Mikroyapı ve Aşınma Özelliklerinin Araştırılması %A Mustafa KAPTANOĞLU , Mehmet EROĞLU %T Ferroniyobyum ve Ferrobor İçeren Tozaltı Kaynak Tozları ile Elde Edilen Kaplamaların Mikroyapı ve Aşınma Özelliklerinin Araştırılması %D 2017 %J Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi %P -1309-1751 %V 20 %N 1 %R doi: 10.17780/ksujes.292373 %U 10.17780/ksujes.292373
ISNAD KAPTANOĞLU, Mustafa , EROĞLU, Mehmet . "Ferroniyobyum ve Ferrobor İçeren Tozaltı Kaynak Tozları ile Elde Edilen Kaplamaların Mikroyapı ve Aşınma Özelliklerinin Araştırılması". Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi 20 / 1 (Nisan 2017): 64-75. http://dx.doi.org/10.17780/ksujes.292373