In this study, the porosity problem that occurs during the joining of TWIP and Martensitic steels, which are two important steels from the AHSS steel family, was investigated. The effects of welding current and welding duration on the formation of porosity were investigated. Macro and microscopic examination of the porosity was made and the amount of formation of the porosity as an area was graphically created in terms of welding parameters. According to the results, the amount of porosity increased as the welding time and welding current increased. The highest porosity amount was 16.2% in 30 period welding time and 12 kA welding current.
Resistance spot welding porosity formation TWIP steel Martensitic steel
Bu çalışmada, AHSS çelik ailesinden iki önemli çelik olan TWIP ve Martenzitik çeliklerinin birleştirilmesi esnasında oluşan porozite problemi araştırılmıştır. Kaynak akımı ve kaynak süresinin porozite oluşumuna etkisi incelenmiştir. Porozitenin makro ve mikroskopik incelenmesi yapılmış ve porozitenin alan olarak oluşum miktarı kaynak parametreleri açısından incelenerek grafiksel olarak elde edilmiştir. Elde edilen bulgulara göre, kaynak süresi ve kaynak akımı arttıkça porozite miktarı artmıştır. En yüksek porozite miktarı 16.2% olarak 30 periyot kaynak süresi ve 12 kA kaynak akımında gerçekleşmiştir.
Elektrik direnç nokta kaynağı porozite oluşumu TWIP çeliği Martenzitik çelik
Birincil Dil | Türkçe |
---|---|
Konular | Mühendislik |
Bölüm | Araştırma Makalesi |
Yazarlar | |
Erken Görünüm Tarihi | 9 Haziran 2022 |
Yayımlanma Tarihi | 9 Haziran 2022 |
Gönderilme Tarihi | 15 Kasım 2021 |
Kabul Tarihi | 28 Şubat 2022 |
Yayımlandığı Sayı | Yıl 2022 Cilt: 63 Sayı: 707 |
Derginin DergiPark'a aktarımı devam ettiğinden arşiv sayılarına https://www.mmo.org.tr/muhendismakina adresinden erişebilirsiniz.
ISSN : 1300-3402
E-ISSN : 2667-7520