KARAÇAM ODUNUNDAN ÜRETİLEN ÇAPRAZ LAMİNE AHŞABIN SEÇİLMİŞ MEKANİK ÖZELLİKLERİ ÜZERİNE RUTUBETİN ETKİSİ

Aydanur Hıdır; Bekir Cihad Bal; Ela Avşaroğlu

doi:10.17780/ksujes.1396980

EN TR

THE EFFECT OF MOISTURE ON SELECTED MECHANICAL PROPERTIES OF CROSS-LAMINATED TIMBER MANUFACTURED FROM BLACK PINE WOOD

Abstract

In recent years, interest in wooden and cross-laminated Timber (CLT) materials has begun to increase. CLT is widely used in the construction of wooden structures in many countries. This material has also begun to be used in the construction of multi-storey buildings. Structural wooden materials used in the construction of multi-storey buildings must have high mechanical performance. However, wood is a material whose mechanical performance changes when it gets moisture. The aim of this study is to determine the effect of moisture on selected mechanical properties of CLT material produced from Black pine wood. For this purpose, 3-layer cross-laminated wood is produced using polyurethane glue. The produced building material was subjected to selected mechanical tests in both air-dry and wet states. Three-point bending strength, modulus of elasticity, deformation at bending, bonding strength, and nail withdrawal resistance of the CLT material were determined. According to the data obtained; It was determined that the bending strength, modulus of elasticity, nail withdrawal resistance and bonding strength of the air-dry test samples were 127%, 118%, 35% and 87% higher, respectively, than those of the wet test samples. It was determined that the bending deformation amount of the wet test samples was 52% higher than that of the dry test samples.

Keywords

KARAÇAM ODUNUNDAN ÜRETİLEN ÇAPRAZ LAMİNE AHŞABIN SEÇİLMİŞ MEKANİK ÖZELLİKLERİ ÜZERİNE RUTUBETİN ETKİSİ

Öz

Son yıllarda ahşap ve çapraz lamine ahşap malzemeye ilgi giderek artmaya başlamıştır. Çapraz lamine ahşap birçok ülkede ahşap yapıların inşasında fazlaca kullanılmaktadır. Bu malzeme çok katlı binaların inşasında da kullanılmaya başlanmıştır. Çok katlı binaların inşasında kullanılan yapısal ahşap malzemelerin mekanik performansının yüksek olması gerekir. Ancak ahşap malzeme rutubet aldığı zaman mekanik performansı değişen bir malzemedir. Bu çalışmanın amacı, karaçam kerestesinden üretilen çapraz lamine ahşap malzemenin, seçilmiş mekanik özellikleri üzerine rutubetin etkisini belirlemektir. Bu amaç için, 3 tabakalı çapraz lamine ahşap poliüretan tutkalı kullanılarak üretilmiştir. Üretilen yapı malzemesi hem hava kurusu hem de yaş halde mekanik testlere tabi tutulmuştur. Çapraz lamine ahşap malzemenin 3 nokta eğilme direnci, elastisite modülü, eğilmede deformasyon miktarı, yapışma direnci, çivi tutma direnci tespit edilmiştir. Elde edilen verilere göre; hava kurusu haldeki test örneklerinin eğilme direnci, elastisite modülü, çivi tutma direnci ve makaslama direnci yaş haldeki test örneklerinden sırasıyla %127, %118, %35 ve%87 daha yüksek olduğu tespit edilmiştir. Yaş haldeki test örneklerinin eğilmede deformasyon miktarının kuru haldeki test örneklerine göre %52 daha fazla olduğu tespit edilmiştir.

Anahtar Kelimeler

References

Amin, Y., Adji, R. P., Lubis, M. A. R., Nugroho, N., Bahtiar, E. T., Dwianto, W., & Karlinasari, L. (2023). Effect of Glue Spread on Bonding Strength, Delamination, and Wood Failure of Jabon Wood-Based Cross-Laminated Timber Using Cold-Setting Melamine-Based Adhesive. Polymers, 15(10), 2349. DOI: 10.3390/polym15102349.
Artun, H. (2021). Çapraz Lamine Ahşap (CLT) Malzemenin Bina Enerji Performansına Etkisi: Trabzon İli Örneği. Yüksek Lisans Tezi. Avrasya Üniversitesi. Fen Bilimleri Enstitüsü. İstanbul, 156s.
Bal, B. C., Özdemir, F., & Altuntaş, E. (2013). Masif ağaç malzeme ve tabakalı kaplama kerestenin vida tutma direnci üzerine karşılaştırmalı bir çalışma. Düzce Üniversitesi Orman Fakültesi Ormancılık Dergisi, 9(2), 14-22.
Bal, B. C. & Kılavuz, M. (2015). İlk Mobilya, Selçuk Üniversitesi Teknik Online Dergisi, (özel sayı): 56-69. ISSN:1302-6178
Bal, B. C. (2016). The effect of moisture content on the screw holding capacity of birch and pine plywood. In International Forestry Symposium (pp. 1020-1025) Kastamonu, Türkiye.
Barutçu, N. (2020). Çapraz Lamine ahşap Ve Betonarme Taşıyıcı Sistemli Tekil Konut Yapılarının Çevresel Etkilerinin Karşılaştırılmalı Değerlendirmesi. Yüksek Lisans Tezi. İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, İstanbul, 229s.
Ceylan, A. (2021) Çapraz Lamine Ahşap Panel Yapı Sistemleri ve Birleşim Özelliklerinin Deneysel İncelenmesi. Doktora Tezi. Yıldız Teknik Üniversitesi, Fen Bilimleri Enstitüsü, İstanbul.
Çavuş, V. (2019). Mühendislik Ürünü Ağaç Malzemelerde Yükselen Trend; Çapraz Tabakalanmış Kereste. Bartın Orman Fakültesi Dergisi, 21 (2), 560-569. DOI: 10.24011/barofd.518169.

Gülcemal, (2019) Sarıçam Ve Göknar Odunlarından Elde Edilen Lamine ve Çapraz Lamine Kirişlerin Mukavemetinin Karşılaştırılması Ve İyileştirilmesi. Yüksek Lisans Tezi. Bartın Üniversitesi. Fen Bilimleri Enstitüsü. Bartın.
Hekimoğlu, V. (2014). Göknar Ve Sarıçam Odunlarından Nanokil İlaveli Çapraz Lamine Kereste Üretim Olanaklarının İncelenmesi. Yüksek Lisans Tezi. Bartın Üniversitesi, Fen Bilimleri Enstitüsü, Bartın, 75s. https://acikbilim.yok.gov.tr/handle/20.500.12812/594289.
Hıdır, A. , Bal, B. C. & Avşaroğlu, E. (2022). Film kaplı kontrplağın bazı mekanik özellikleri üzerine rutubet içeriğinin etkisi, Mobilya ve Ahşap Malzeme Araştırmaları Dergisi, 5(2),102-109.DOI: 10.33725/mamad.1186623
Hu, C., Dengyun, T., Liao, Y., & Zhang, W. (2016). Feasibility of Manufacturing Cross-laminated Timber Using Fast-grown Small Diameter Eucalyptus lumbers. Construction and Building Materials Journal, 132, 508-515. https://doi.org/10.1016/j.conbuildmat.2016.12.027.
Karacabeyli E. and Douglas B., (2013) CLT: handbook cross-laminated timber, FPInnovations.
Knorz, M., Torno, S., & van de Kuilen, J. W. (2017), Bonding quality of industrially produced cross-laminated timber (CLT) as determined in delamination tests. Construction and Building Materials, 133, 219-225. https://doi.org/10.1016/j.conbuildmat.2016.12.057.
Jucienė, M., Dobilaitė, V., & Albrektas, D. (2023). An Investigation of the Impact of Water on Certain of the Mechanical and Physical Properties of Laminated Veneer Lumber (LVL) as Used in Construction. Applied Sciences, 13(2), 925. https://doi.org/10.3390/app13020925.
Mahsereci A.H. (2023), Karaçam odunundan üretilen çapraz tabakalı kereste (ÇTK) malzemenin farklı koşullardaki mekanik dayanımı üzerine bir araştırma. Yüksek Lisans Tezi. Kahramanmaraş Sütçü İmam Üniversitesi, Fen Bilimleri Enstitüsü, Kahramanmaraş, 79s.
Mengeloğlu, F. & Kurt, R. (2004). Mühendislik ürünü ağaç malzemeler 1 tabakalanmış kaplama kereste (TAK) ve tabakalanmış ağaç malzeme (TAM). KSÜ Fen ve Mühendislik Dergisi, 7(1), 39-44.
Oran, B. (2012). Hindistan Cevizi (Cocos nucifera L.) Odunu İle Üretilen Çapraz Yapıştırılmış Lamine Kerestelerin Bazı Teknolojik Özellikleri. Yüksek Lisans Tezi. Karadeniz Teknik Üniversitesi, Fen Bilimleri Enstitüsü, Trabzon, 89s. https://acikbilim.yok.gov.tr/handle/20.500.12812/480008.
Özan, Z. E. (2017) Isıl İşlem Görmüş Ahşap Malzemenin Çapraz Lamine Kereste Üretiminde Kullanım Olanaklarının Araştırılması. Yüksek Lisans Tezi. Bartın Üniversitesi, Fen Bilimleri Enstitüsü, Bartın, 61s. http://hdl.handle.net/11772/405,
Şanlı, E. (2020) Çapraz Lamine Ahşabın Strüktürel Kullanımının Ve Performans Özelliklerinin İncelenmesi. Yüksek Lisans Tezi. Karadeniz Teknik Üniversitesi. Fen Bilimleri Enstitüsü, İstanbul, 437s.
TS 3459, (1980), Odunda Liflere Paralel doğrultuda Makaslama Dayanımının Tayini, TSE, Ankara.
TS EN 310, (1999), Ahşap esaslı levhalar- Eğilme dayanımı ve eğilme elastikiyet modülünün tayini, TSE, Ankara.
TS EN 322, (1999), Ahşap Esaslı Levhalar-Rutubet Miktarının Tayini, TSE, Ankara.
TS EN 323, (1999), Ahşap esaslı levhalar-Birim hacim ağırlığının tayini, TSE, Ankara.
TS EN 13446, (2005), Ahşap esaslı levhalar-bağlayıcıların geri çıkma kapasitesinin tayini, TSE, Ankara.
URL 1 (2023) Cross-Laminated Timber (CLT): Feature and Benefits https://theconstructor.org/building/cross-laminated-timber-clt-features-and- benefits/565439/
Yang, S., Li, H., Fei, B., Zhang, X., & Wang, X. (2022). Bond quality and durability of cross-laminated flattened bamboo and timber (CLBT). Forests, 13(8), 1271. https://doi.org/10.3390/f13081271.
Wang, J. B., Wei, P., Gao, Z., & Dai, C. (2018). The evaluation of panel bond quality and durability of hem-fir cross-laminated timber (CLT). European Journal of Wood and Wood Products, 76, 833-841. https://doi.org/10.1007/s00107-017-1283-7.

Details

Primary Language

Turkish

Subjects

Construction Materials , Composite and Hybrid Materials , Wood Based Composites

Journal Section

Research Article

Authors

Aydanur Hıdır
0000-0003-3449-1728
Türkiye

Bekir Cihad Bal
0000-0001-7097-4132
Türkiye

Ela Avşaroğlu ^*
0000-0001-9373-1192
Türkiye

Publication Date

June 3, 2024

Submission Date

November 28, 2023

Acceptance Date

March 11, 2024

Published in Issue

Year 2024 Volume: 27 Number: 2

DOI

https://doi.org/10.17780/ksujes.1396980

IZ

https://izlik.org/JA75PG74ZX

Cite

RIS / Bibtex

APA

Hıdır, A., Bal, B. C., & Avşaroğlu, E. (2024). KARAÇAM ODUNUNDAN ÜRETİLEN ÇAPRAZ LAMİNE AHŞABIN SEÇİLMİŞ MEKANİK ÖZELLİKLERİ ÜZERİNE RUTUBETİN ETKİSİ. Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi, 27(2), 502-510. https://doi.org/10.17780/ksujes.1396980

Cited By

Kavak kaplamadan üretilen tabakalı kaplama kerestenin mekanik özellikleri üzerine rutubet içeriğinin etkisinin değerlendirilmesi

Mobilya ve Ahşap Malzeme Araştırmaları Dergisi

https://doi.org/10.33725/mamad.1697367

Tarihi Ahşap Çatı Birleşim Davranışının Deneysel İncelenmesi

Turkish Journal of Civil Engineering

https://doi.org/10.18400/tjce.1719905