Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi

İbrahim Bektaş; Gonca Düzkale Sözbir; Bekir Cihad Bal; Ertuğrul Altuntaş

doi:10.17780/ksujes.287672

EN TR

Effects of the termal and pressurised thermal modification treatments on chemical properties of the poplar woods

Öz

In this study, it was planned to extend physical life of poplar wood (Populus usbekistanica), less natural durability and fast-growing tree species, with eco-friendly thermal treatment method. For this reason, poplar wood test samples were subjected to thermal and thermal-pressure modifications. The effects of the thermally modificated and thermally compressed on chemical properties of the poplar woods are investigated. The results indicated that, due to the applied 160^oC above temperatures caused degradation in hemicellulose content, holocellulose (cellulose + hemicelluloses) content of the samples was decreased. At the same time, there were no remarkable changes in holocellulose content of the heat-compressed poplar wood compared with the control samples. Since the extractive substances are not taken into account, it was seen obviously that as temperature increases, the lignin content of the poplar samples also increased. As a result of heat-treated and heat-compressed modifications, it was observed that the heat treatment process below 160^oC has no degradation on the chemical properties of poplar woods; however, degradation of the chemical properties was occurred, when the poplar woods were exposed above 160^oC. Finally, it was seen that holocellulose content decreases as the duration of the treatment increases.

Anahtar Kelimeler

Thermal process,thermal pressure,poplar wood,chemical properties

Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi

Öz

Bu çalışmada, hızlı büyüyen ve doğal dayanıklılığı az fakat önemli türlerimizden biri olan kavak odunun (Populus usbekistanica) çevreye dost termal işlemlerle ömrünün uzatılması planlandı. Bu amaçla, yapılan testlerle hazırlanan kavak odunu numuneleri termal ve basınçlı termal modifikasyona maruz bırakıldı. Termal ve basınçlı termal modifikasyonun kavak odununun kimyasal özellikleri üzerine etkisi araştırıldı. Araştırma sonuçları, 160^oC’nin üzerindeki sıcaklıklarda odunda hemiselüloz içeriğinin bozunmasından dolayı, holoselüloz (Selüloz+hemiselüloz) miktarının azaldığını (% 10.8) gösterdi. Aynı zamanda, basınçlı termal modifikasyon işlemine maruz kalmış kavak örneklerinin holoselüloz içeriğinin de % 2.2 oranında azaldığı belirlendi. Ekstraktif maddelerin dikkate alınmamasından dolayı, sıcaklık artışlarının lignin miktarını da arttırdığı görüldü. Termal ve basınçlı termal modifikasyonu işlemlerinin bir sonucu olarak, 160^oC’nin üzerinde uygulanan sıcaklık derecelerinde kimyasal içeriklerde bir degredasyon oluşmasına karşın, 160^oC ve altındaki sıcaklıklarda kavak odunu numunelerinin kimyasal özellikleri üzerinde önemli derecede bir bozunmanın meydana gelmediği gözlendi. Sonuç olarak, termal işlem uygulama sürelerinin artması ile, test numunelerinin holoselüloz içeriklerinde önemli bir azalma olduğu görüldü.

Anahtar Kelimeler

Termal işlem,termal basınç,kavak,kimyasal özellikler

Kaynakça

Akyıldız, M.H., Ateş, S., and Özdemir, H., (2009), “Technological and chemical properties of heat-treated Anatolian black pine wood”, African Journal of Biotechnology, 8(11): 2565-2572.
Atik, C., (1995), “Titrek Kavak (Populus tremula L.) ve Kağıt Sanayii”, İ.Ü. Fen Bilimleri Enstitüsü Yüksek Lisans Tezi, İstanbul, sayfa: 1-71.
Bal, B.C., Bektaş, İ, 2012, The effects of heat treatment on the physical properties of juvenile wood and mature wood of Eucalyptus grandis. Bioresources 7(4): 5117-5127.
Bal, B.C., 2013a, Effects of Heat Treatment on the Physical Properties of Heartwood and Sapwood of Cedrus Libani. Bioresources 8(1):211-219.
Bal. B.C., 2013b, A Comparative Study of the Physical Properties of Thermally Treated Poplar Wood and Plane Wood, Bioresources 8(4):6493-6500.
Balatinecz, J., Kretschmann, D.E., (2001), “Properties and Utilization of Poplar Wood, Poplar Culture in North America”, The 21st session of the International Poplar Commission, National Research Council of Canada.
Batista, D.C., Muniz, G.I.B., Oliveira, J.T.S., Paes, J.B., Nisgoski, S., 2016. “Effect of the Brazilian thermal modification process on the chemical composition of Eucalyptus grandis juvenile wood – Part 1: Cell wall polymers and extractives contents”, Maderas, Cienc. tecnol. vol.18 no.2, http://dx.doi.org/10.4067/S0718-221X2016005000025
Birler, A.S., (2010), “Türkiye’de kavak yetiştirme fidanlık – ağaçlandırma – koruma hâsılat – ekonomi – odun özellikleri”, Çevre ve Orman Bakanlığı Yayın No: 393 ISSN: 1300-395X, Araştırma Müdürlüğü Yayın No: 262, çeşitli yayınlar serisi No: 22, İzmit, sayfa:224.

Cabalova, I., Kacík, F., Tribulova, T., (2016), “The Effects of Heat Treatment on the Chemical Alterations of Oak Wood”, Trans Tech Publications, Key Engineering Materials.
Esteves, B.M., Pereira, H.M., (2009), “Heat treatment of wood”, Bioresources”, 4(1).370-404.
Gündüz, G., Aşık, A., Aydemir, D., Kılıç, A., (2015), “Bakteriyel selüloz üretimi ve karakterizasyonu”, Düzce Üniversitesi Ormancılık Dergisi, 10(2), 1-10.
Hill, C., (2006), “Wood modification –chemical, thermal and other processes”, Wiley Series in Renewable Resources, Jhon Wiley & Sons. Ltd.
Huş, Savni, (1959), “Kavak odununun kimyevi yönden değerlendirme imkanlari”, İ.Ü Orman Fakültesi Dergisi, Seri B, Cilt IX, Sayı II, sayfa: 46.
Militz, H., (2002), “Thermal treatment of wood. European process and their background”, In: Cardiff-Wales, IRG/WP02 40241 33rd. Annual Meeting.
Öner, N., Aslan, S., (2002), “Titrek kavak (Populus tremula l.) odununun teknolojik özellikleri ve kullanım yerleri”, Süleyman Demirel Üniversitesi, Orman Fakültesi Dergisi, Seri: A, Sayı: 1, ISSN: 1302-7085, Sayfa:135-146.
Patzelt, M., Emsenhuber, G. and Stingl, R., (2003), “Color measurement as means of quality control of thermally treated wood”, Abstracts of the First European Conference on Wood Modification, Chent, Belguim.
Shafizadeh, F., Chin, P.P.S., (1977), “Wood techonology; Chemical Aspects”, American Chemical Society. Washington.
Toplu, F., (1999), “Fırat Kavağı”, Güneydoğu Anadolu Ormancılık Araştırma Enstitüsü Yayınları, Çeşitli Yayınlar Serisi No:1, Cilt No: 688, Sayfa: 44-49.
Wenzl. H., (1970), “The Chemical Technology of Wood”, Academic press, New York, p: 684.
Yıldız, S., (2002), “Isıl İşlem Uygulanan Doğu Kayını Ve Doğu Ladini Odunlarının Fiziksel Teknolojik ve Kimyasal Özellikleri”, Doktora Tezi, K.T.Ü. Fen Bilimleri Enstitüsü, Trabzon.

Ayrıntılar

Birincil Dil

Türkçe

Konular

Mühendislik

Bölüm

Araştırma Makalesi

Yazarlar

İbrahim Bektaş
Kahramanmaraş Sürçü İmam Üniversitesi
Türkiye

Gonca Düzkale Sözbir
Kahramanmaraş Sürçü İmam Üniversitesi
Türkiye

Bekir Cihad Bal
Kahramanmaraş Sürçü İmam Üniversitesi
Türkiye

Ertuğrul Altuntaş
Kahramanmaraş Sürçü İmam Üniversitesi
Türkiye

Yayımlanma Tarihi

27 Nisan 2017

Gönderilme Tarihi

24 Ocak 2017

Kabul Tarihi

-

Yayımlandığı Sayı

Yıl 2017 Cilt: 20 Sayı: 1

DOI

https://doi.org/10.17780/ksujes.287672

IZ

https://izlik.org/JA57SH65LJ

Kaynak Göster

RIS / Bibtex

APA

Bektaş, İ., Düzkale Sözbir, G., Bal, B. C., & Altuntaş, E. (2017). Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi. Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi, 20(1), 31-37. https://doi.org/10.17780/ksujes.287672

AMA

1.Bektaş İ, Düzkale Sözbir G, Bal BC, Altuntaş E. Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi. Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi. 2017;20(1):31-37. doi:10.17780/ksujes.287672

Chicago

Bektaş, İbrahim, Gonca Düzkale Sözbir, Bekir Cihad Bal, ve Ertuğrul Altuntaş. 2017. “Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi”. Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi 20 (1): 31-37. https://doi.org/10.17780/ksujes.287672.

EndNote

Bektaş İ, Düzkale Sözbir G, Bal BC, Altuntaş E (01 Nisan 2017) Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi. Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi 20 1 31–37.

IEEE

[1]İ. Bektaş, G. Düzkale Sözbir, B. C. Bal, ve E. Altuntaş, “Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi”, Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi, c. 20, sy 1, ss. 31–37, Nis. 2017, doi: 10.17780/ksujes.287672.

ISNAD

Bektaş, İbrahim - Düzkale Sözbir, Gonca - Bal, Bekir Cihad - Altuntaş, Ertuğrul. “Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi”. Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi 20/1 (01 Nisan 2017): 31-37. https://doi.org/10.17780/ksujes.287672.

JAMA

1.Bektaş İ, Düzkale Sözbir G, Bal BC, Altuntaş E. Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi. Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi. 2017;20:31–37.

MLA

Bektaş, İbrahim, vd. “Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi”. Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi, c. 20, sy 1, Nisan 2017, ss. 31-37, doi:10.17780/ksujes.287672.

Vancouver

1.İbrahim Bektaş, Gonca Düzkale Sözbir, Bekir Cihad Bal, Ertuğrul Altuntaş. Kavak odununun kimyasal özellikleri üzerine termal ve basınçlı termal modifikasyon işlemlerinin etkisi. Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi. 01 Nisan 2017;20(1):31-7. doi:10.17780/ksujes.287672

Cited By

VAKUM ATMOSFERİNDE YAPILAN ISIL İŞLEMİN KAVAK ODUNUNUN MEKANİK ÖZELLİKLERİ ÜZERİNE ETKİSİNİN ARAŞTIRILMASI

Kahramanmaraş Sütçü İmam Üniversitesi Mühendislik Bilimleri Dergisi

https://doi.org/10.17780/ksujes.886540