Cylindrical steel tanks are widely used to water store and for cooling
in nuclear power plants. The seismic behaviour of liquid storage tanks is very
complicated due to the hydrodynamic pressures of the fluids in them. In this
paper, the epoxy-carbon coating method is suggested to improve of seismic
performance of cylindrical steel tanks. Composite epoxy-carbon materials are
widely used for winding thin walled cylindrical steel structures. After tank
had coated with epoxy–carbon composite material, it was observed that
Equivalent (von-Mises) stresses significantly decreased. The maximum hoop
stress in the unprotected tank is 81.92 MPa, while the maximum stress is
reduced to 44.77 MPa after it was coated with the epoxy-carbon.
Silindirik çelik sıvı tankları nükleer enerji santrallerde su depolamak ve soğutma amacıyla yaygın olarak kullanılmaktadır. Sıvı depolama tanklarının sismik davranışları, içlerdikleri akışkanların hidrodinamik basınçlarından dolayı çok karmaşıktır. Bu makalede, silindirik çelik sıvı tanklarının sismik performansının iyileştirilmesi için epoksi-karbon ile kaplama yöntemi önerilmiştir. Kompozit epoksi-karbon malzemeler, ince duvarlı silindirik çelik yapıların sarılması için yaygın olarak kullanılmaktadır. Deponun epoksi-karbon kompozit malzeme ile kaplanmasından sonra, Equivalent (von-Mises) stresin ciddi şekilde azaldığı gözlemlenmiştir. Korunmasız tanktaki maksimum çember gerilimi 81.92 MPa iken, maksimum çevre gerilimi epoksi-karbon ile kaplandıktan sonra 44.77 MPa'ya düşmüştür
Birincil Dil | İngilizce |
---|---|
Konular | İnşaat Mühendisliği |
Bölüm | İnşaat Mühendisliği |
Yazarlar | |
Yayımlanma Tarihi | 24 Aralık 2018 |
Gönderilme Tarihi | 9 Temmuz 2018 |
Yayımlandığı Sayı | Yıl 2018Cilt: 21 Sayı: 4 |